Electro Galvanization

After all manufacturing processes are finished Electro zinc plated or chromed are applicable on every thickness of material. It is recommended to use only in dry environments . Coating thickness 8-12 microns.

TS 149


Hot-dip galvanization is a form of galvanization. It is the process of coating iron and steel with zinc, which alloys with the surface of the base metal when immersing the metal in a bath of molten zinc . Coating thickness average 40-60 microns .

TS 914 EN ISO 1461


Pre-galvanized ( mill galvanized steel)

Galvanized flat sheet thickness fused steel sheets up to 2.5mm immersed in a zinc bath coating material. Coating thickness 15-20 microns.

TS 822 EN 10142